dupont performance polymers zytel® 7335f nc010 nylon 6 (unverified data**) 物性表
物理性能
額定值 (公制)
額定值 (英制)
測(cè)試方法
|
密度
|
1.13 g/cc
|
0.0408 lb/in3
|
dam; iso 1183
|
|
water absorption
|
3.0 ％
@temperature 23.0 °c
|
3.0 ％
@temperature 73.4 °f
|
equilibrium 50％rh; dam; iso 62, similar to
|
|
|
9.0 ％
@temperature 23.0 °c
|
9.0 ％
@temperature 73.4 °f
|
saturation, immersed; dam; iso 62, similar to
|
|
線性成型收縮率
|
0.0075 cm/cm
@thickness 1.60 mm
|
0.0075 in/in
@thickness 0.0630 in
|
dam
|
|
|
0.010 cm/cm
@thickness 3.20 mm
|
0.010 in/in
@thickness 0.126 in
|
dam
|
|
線性成型收縮率,flow
|
0.0060 cm/cm
@thickness 2.00 mm
|
0.0060 in/in
@thickness 0.0787 in
|
dam; iso 294-4
|
|
線性成型收縮率，橫向
|
0.0080 cm/cm
@thickness 2.00 mm
|
0.0080 in/in
@thickness 0.0787 in
|
dam; iso 294-4
|
機(jī)械性能
額定值 (公制)
額定值 (英制)
測(cè)試方法
|
抗張強(qiáng)度(屈服)
|
55.0 mpa
@temperature 23.0 °c
|
7980 psi
@temperature 73.4 °f
|
50％rh; iso 527
|
|
|
90.0 mpa
@temperature 23.0 °c
|
13100 psi
@temperature 73.4 °f
|
dam; iso 527
|
|
伸長(zhǎng)率 (斷裂)
|
9.0 ％
@temperature 23.0 °c
|
9.0 ％
@temperature 73.4 °f
|
dam; nominal; iso 527
|
|
|
15 ％
@temperature 23.0 °c
|
15 ％
@temperature 73.4 °f
|
50mm/min; dam; iso 527
|
|
|
>= 50 ％
@temperature 23.0 °c
|
>= 50 ％
@temperature 73.4 °f
|
50mm/min; 50％rh; iso 527
|
|
|
>= 50 ％
@temperature 23.0 °c
|
>= 50 ％
@temperature 73.4 °f
|
50％rh; nominal; iso 527
|
|
elongation at yield
|
3.8 ％
@temperature 23.0 °c
|
3.8 ％
@temperature 73.4 °f
|
dam; iso 527
|
|
|
24 ％
@temperature 23.0 °c
|
24 ％
@temperature 73.4 °f
|
50％rh; iso 527
|
|
拉伸模量
|
1.40 gpa
@temperature 23.0 °c
|
203 ksi
@temperature 73.4 °f
|
50％rh; iso 527
|
|
|
3.60 gpa
@temperature 23.0 °c
|
522 ksi
@temperature 73.4 °f
|
dam; iso 527
|
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度
|
6.00 j/cm2
@temperature -30.0 °c
|
28.6 ft-lb/in2
@temperature -22.0 °f
|
50％rh; iso 179/1eu
|
|
|
7.00 j/cm2
@temperature 23.0 °c
|
33.3 ft-lb/in2
@temperature 73.4 °f
|
dam; iso 179/1eu
|
|
|
11.0 j/cm2
@temperature -30.0 °c
|
52.3 ft-lb/in2
@temperature -22.0 °f
|
dam; iso 179/1eu
|
|
|
12.0 j/cm2
@temperature 23.0 °c
|
57.1 ft-lb/in2
@temperature 73.4 °f
|
50％rh; iso 179/1eu
|
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度
|
0.250 j/cm2
@temperature -30.0 °c
|
1.19 ft-lb/in2
@temperature -22.0 °f
|
dam; iso 179/1ea
|
|
|
0.300 j/cm2
@temperature -30.0 °c
|
1.43 ft-lb/in2
@temperature -22.0 °f
|
50％rh; iso 179/1ea
|
|
|
0.450 j/cm2
@temperature 23.0 °c
|
2.14 ft-lb/in2
@temperature 73.4 °f
|
dam; iso 179/1ea
|
|
|
1.80 j/cm2
@temperature 23.0 °c
|
8.57 ft-lb/in2
@temperature 73.4 °f
|
50％rh; iso 179/1ea
|
電氣性能
額定值 (公制)
額定值 (英制)
測(cè)試方法
|
體積電阻率
|
1.00e+11 ohm-cm
@temperature 23.0 °c
|
1.00e+11 ohm-cm
@temperature 73.4 °f
|
50％rh; astm d257
|
|
|
1.00e+11 ohm-cm
@temperature 23.0 °c
|
1.00e+11 ohm-cm
@temperature 73.4 °f
|
50％rh; iec 60093
|
|
|
>= 1.00e+15 ohm-cm
@temperature 23.0 °c
|
>= 1.00e+15 ohm-cm
@temperature 73.4 °f
|
dam; iec 60093
|
|
|
1.00e+17 ohm-cm
@temperature 23.0 °c
|
1.00e+17 ohm-cm
@temperature 73.4 °f
|
dam; astm d257
|
|
|
1.00e+17 ohm-cm
@temperature 23.0 °c
|
1.00e+17 ohm-cm
@temperature 73.4 °f
|
dam; iec 60093
|
|
surface resistance
|
1.00e+11 ohm
@temperature 23.0 °c
|
1.00e+11 ohm
@temperature 73.4 °f
|
50％rh; astm d257
|
|
|
1.00e+11 ohm
@temperature 23.0 °c
|
1.00e+11 ohm
@temperature 73.4 °f
|
50％rh; iec 60093
|
|
|
1.00e+13 ohm
@temperature 23.0 °c
|
1.00e+13 ohm
@temperature 73.4 °f
|
dam; astm d257
|
|
介電常數(shù)
|
3.3
@frequency 1.00e+6 hz, temperature 23.0 °c
|
3.3
@frequency 1.00e+6 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
3.6
@frequency 100 hz, temperature 23.0 °c
|
3.6
@frequency 100 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
3.6
@frequency 1000 hz, temperature 23.0 °c
|
3.6
@frequency 1000 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
4.2
@frequency 100 hz, temperature 23.0 °c
|
4.2
@frequency 100 hz, temperature 73.4 °f
|
dam; iec 60250
|
|
介電強(qiáng)度
|
13.5 kv/mm
@thickness 3.20 mm, temperature 23.0 °c
|
343 kv/in
@thickness 0.126 in, temperature 73.4 °f
|
50％rh; short time; astm d149
|
|
|
16.3 kv/mm
@thickness 3.20 mm, temperature 23.0 °c
|
414 kv/in
@thickness 0.126 in, temperature 73.4 °f
|
dam; short time; astm d149
|
|
耗散因數(shù)
|
0.010
@frequency 1000 hz, temperature 23.0 °c
|
0.010
@frequency 1000 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
0.010
@frequency 100 hz, temperature 23.0 °c
|
0.010
@frequency 100 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
0.020
@frequency 1.00e+6 hz, temperature 23.0 °c
|
0.020
@frequency 1.00e+6 hz, temperature 73.4 °f
|
dam; astm d150
|
|
|
0.030
@frequency 100 hz, temperature 23.0 °c
|
0.030
@frequency 100 hz, temperature 73.4 °f
|
dam; iec 60250
|
|
|
0.11
@frequency 1.00e+6 hz, temperature 23.0 °c
|
0.11
@frequency 1.00e+6 hz, temperature 73.4 °f
|
50％rh; astm d150
|
|
|
0.23
@frequency 1000 hz, temperature 23.0 °c
|
0.23
@frequency 1000 hz, temperature 73.4 °f
|
50％rh; astm d150
|
|
|
0.37
@frequency 100 hz, temperature 23.0 °c
|
0.37
@frequency 100 hz, temperature 73.4 °f
|
50％rh; astm d150
|
|
相比耐漏電起痕指數(shù)(cti)
|
600 v
@temperature 23.0 °c
|
600 v
@temperature 73.4 °f
|
dam; iec 60112
|